TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Beta Forged

Category	Metal , Nonferrous Metal , Titanium Alloy , Beta Titanium Alloy
Manufacturer	TIMET
Trade Name	TIMETAL®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Beta Forged.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Low Cost, Multipurpose Alloy. Tensile/toughness property data below for Beta Forged, RA material.Features: Properties and processing characteristics equivalent to or better than TIMETAL 6-4, but with significantly higher stiffness (elastic modulus). Due to the use of iron as the beta stabilizer, the alloy has lower formulation costs than TIMETAL 6-4. The combination of reasonable cost and excellent mechanical properties make TIMETAL 62S a practical substitute for many engineering materials.Typical heat treatment for this alloy: Mill Anneal at 760°C for 1-2 hrs, air cool Data provided by TIMET.

Physical Properties	Metric	English	Comments
Density	4.44 g/cc	0.160 lb/in³	Typical

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	986 MPa	143000 psi	Typical Longitudinal
	1000 MPa	145000 psi	Typical Transverse
Tensile Strength, Yield	945 MPa @Strain 0.200 %	137000 psi @Strain 0.200 %	Longitudinal, typical
	952 MPa @Strain 0.200 %	138000 psi @Strain 0.200 %	Transverse, typical
Elongation at Break	11 %	11 %	Typical Transverse in 2 in (50 mm)
	15 %	15 %	Typical Longitudinal in 2 in (50 mm)
Reduction of Area	16 %	16 %	Longitudinal
	20 %	20 %	Transverse
Modulus of Elasticity	128 GPa	18600 ksi	Typical
Fracture Toughness	64.0 MPa-m½	58.2 ksi-in½	K(IC); T-L Orientation
	67.0 MPa-m½	61.0 ksi-in½	K(IC); L-T Orientation
Bend Radius, Minimum	4.5 t @Thickness 2.00 mm	4.5 t @Thickness 0.0787 in	Typical; sheet

Thermal Properties	Metric	English
CTE, linear	8.60 µm/m-°C @Temperature 20.0 °C	4.78 µin/in-°F @Temperature 68.0 °F
	9.70 µm/m-°C @Temperature 250 °C	5.39 µin/in-°F @Temperature 482 °F
	10.6 µm/m-°C @Temperature 500 °C	5.89 µin/in-°F @Temperature 932 °F
Specific Heat Capacity	0.500 J/g-°C	0.120 BTU/lb-°F
Thermal Conductivity	8.60 W/m-K	59.7 BTU-in/hr-ft²-°F
Beta Transus	1024 °C	1875 °F

Component Elements Properties	Metric	English	Comments
Aluminum, Al	5.5 - 6.5 %	5.5 - 6.5 %
Carbon, C	<= 0.080 %	<= 0.080 %
Hydrogen, H	<= 0.0125 %	<= 0.0125 %
Iron, Fe	1.3 - 2.0 %	1.3 - 2.0 %
Nitrogen, N	<= 0.040 %	<= 0.040 %
Oxygen, O	0.15 - 0.20 %	0.15 - 0.20 %
Silicon, Si	0.070 - 0.13 %	0.070 - 0.13 %
Titanium, Ti	90.7 - 93 %	90.7 - 93 %	Calculated as remainder

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.000163 ohm-cm	0.000163 ohm-cm

Users viewing this material also viewed the following: