Samsung Cheil Industries Starex® WR-9140 General Purpose ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WR-9140 General Purpose ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength at Break | 42.7 MPa | 6200 psi | ASTM D638 |
| Elongation at Break | 76 % | 76 % | ASTM D638 |
| Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790 |
| Izod Impact, Notched | 4.81 J/cm | 9.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.35 mm |
185 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ISO R-306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | H1 |
| Middle Barrel Temperature | 210 - 230 °C | 410 - 446 °F | H2 |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | H3 |
| Nozzle Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.3 - 147 MPa | 9900 - 21300 psi | |
| Back Pressure | 0.979 - 1.96 MPa | 142 - 284 psi | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- BASF Capron® GR20 20% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Polimeri Europa EDISTIR RK0414 High Impact Polystyrene (HIPS) (discontinued **)
- Formosa Plastics Formolene® L63568U Rotational Molding LLDPE (discontinued **)
- Grupo Repol Dinalon® A1S25 G50 PA66 50% Glass Fiber
- Special Metals BRIGHTRAY® Alloy B Electrical Resistance Alloy
- Solvay MACKAZOLINE® O-V Surfactant
- Teknor Apex Sinpolene GPP1620 Polypropylene
- Dow SE SLR-4630 Solution polymerized Styrene Butadiene Rubber (S-SBR)
- Formosa Plastics Formolene® 1102K Cast and BOPP Film Polypropylene
- Kazanorgsintez P2ES-12 Electrically Conductive Polyethylene Composite
Copyright © lookpolymers.com All Rights Reserved