Toyobo GLAMIDE® TY-791GT 6T-Nylon
| Category | Polymer , Thermoplastic , Nylon , Nylon, Aromatic |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® TY-791GT 6T-Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade TY-791GT is a GF reinforced, aromatic 6T-Nylon. It has a good finish of coating and contains 55% GF.55
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.64 g/cc | 1.64 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 55 % | 55 % | |
| Water Absorption | 0.80 % | 0.80 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm @Thickness 1.00 mm |
0.0010 - 0.0020 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0020 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0020 - 0.0050 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 10 g/10 min | 10 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 105 MPa @Temperature 80.0 °C |
15200 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.0%); ASTM-D638 |
| 120 MPa @Temperature 80.0 °C |
17400 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 165 MPa @Temperature 23.0 °C |
23900 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.0%); ASTM-D638 | |
| 230 MPa @Temperature 23.0 °C |
33400 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 250 MPa @Temperature -40.0 °C |
36300 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.0%); ASTM-D638 | |
| 280 MPa @Temperature -40.0 °C |
40600 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 1.6 % | 1.6 % | Absolute Drying; ASTM-D638 |
| 2.0 % | 2.0 % | Practical Use (Water Absorption 1.0%); ASTM-D638 | |
| Flexural Strength | 160 MPa @Temperature 80.0 °C |
23200 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.0%); ASTM-D790 |
| 180 MPa @Temperature 80.0 °C |
26100 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 280 MPa @Temperature 23.0 °C |
40600 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.0%); ASTM-D790 | |
| 320 MPa @Temperature -40.0 °C |
46400 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.0%); ASTM-D790 | |
| 320 MPa @Temperature 23.0 °C |
46400 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 355 MPa @Temperature -40.0 °C |
51500 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 5.00 GPa @Temperature 80.0 °C |
725 ksi @Temperature 176 °F |
Practical Use (Water Absorption 1.0%); ASTM-D790 |
| 7.50 GPa @Temperature 80.0 °C |
1090 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 13.0 GPa @Temperature 23.0 °C |
1890 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.0%); ASTM-D790 | |
| 15.0 GPa @Temperature -40.0 °C |
2180 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.0%); ASTM-D790 | |
| 16.0 GPa @Temperature 23.0 °C |
2320 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 16.5 GPa @Temperature -40.0 °C |
2390 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 150 MPa | 21800 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.700 J/cm @Temperature -40.0 °C |
1.31 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.850 J/cm @Temperature -40.0 °C |
1.59 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 1.0%); ASTM-D256 | |
| 1.43 J/cm @Temperature 23.0 °C |
2.68 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 1.80 J/cm @Temperature 23.0 °C |
3.37 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 1.0%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 19.0 µm/m-°C | 10.6 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 |
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 1.0%); ASTM-D149 |
| 28.0 kV/mm @Thickness 2.00 mm |
711 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 94 sec | 94 sec | Practical Use (Water Absorption 1.0%); ASTM-D495 |
| 100 sec | 100 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 550 V | 550 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Injection Pressure | 30.0 - 70.0 MPa | 4350 - 10200 psi |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® FF D0 Very Low Density Polyethylene
- Kraton® G1650 + PPE blend (10/90)
- Techmer ES HiFill® PA6 GF/M25 HS L BK 25% Glass/Mineral Filled
- Samyang Triel® 5350 Thermoplastics Polyetherester Elastomer, General Extrusion
- Solvay IGEPAL® CO 977 Surfactant
- Saint-Gobain Tygon® 2001 Plasticizer Free Tubing Formulation
- 3M 4462B Double Coated Polyethylene Foam Tape
- ExxonMobil Exxtral™ MDK310 Performance Polyolefin
Copyright © lookpolymers.com All Rights Reserved