- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Samsung Cheil Industries Starex® SD-0160 Super High Impact Grade ABS
Samsung Cheil Industries Starex® SD-0160 Super High Impact Grade ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SD-0160 Super High Impact Grade ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 13 g/10 min @Load 10.0 kg, Temperature 220 °C |
13 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ASTM D785 |
| Tensile Strength, Yield | 39.3 MPa @Thickness 3.17 mm |
5700 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 87 % @Thickness 3.17 mm |
87 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 60.0 MPa @Thickness 3.17 mm |
8700 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 1.93 GPa @Thickness 3.17 mm |
280 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 4.32 J/cm @Thickness 3.17 mm |
8.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C @Thickness 6.35 mm |
180 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | Unannealed; ISO R 306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 96 % | 96 % | ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.6 - 108 MPa | 9950 - 15600 psi | |
| Back Pressure | 0.689 - 1.38 MPa | 100 - 200 psi | |
| Screw Speed | 60 - 80 rpm | 60 - 80 rpm |
Users viewing this material also viewed the following:
- Polymer Resources PC-HM-FR1-[color]-4 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized with Mold Release
- Eastman D4056-P Polyethylene (discontinued **)
- M. Holland Company AB105 ABS
- LyondellBasell Petrothene® NA860241 Low Density Polyethylene
- Master Bond UV10FL-1 Flexibilized One Component UV Curable Adhesive
- Hexcel® HexWeb® HRH-10/F50 - 3.5 Nonmetallic Flex-Core Honeycomb
- Chosun Refractories HSM-38 Heat-Setting Mortar
- 3M 6035PC 12038 Polyurethane Foam Tape (15 lb./ft3 (239 kg/m3) Series)
- ArcelorMittal HSLA 380 High strength low alloy steel for cold forming, Cold Rolled
Copyright © lookpolymers.com All Rights Reserved