Samsung Cheil Industries Starex® MP-0160RD Metal Plating Grade ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® MP-0160RD Metal Plating Grade ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 44.1 MPa @Thickness 3.17 mm |
6400 psi @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 64.8 MPa @Thickness 3.17 mm |
9400 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.34 GPa @Thickness 3.17 mm |
340 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 2.56 J/cm @Thickness 3.17 mm |
4.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C @Thickness 6.35 mm |
187 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | Unannealed; ISO R 306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 96 % | 96 % | ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.6 - 108 MPa | 9950 - 15600 psi | |
| Back Pressure | 0.689 - 1.38 MPa | 100 - 200 psi | |
| Screw Speed | 60 - 80 rpm | 60 - 80 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV Resistance | <1 Delta E | 300 Hr. Ivory Color; ASTM D4459 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FL920 PC (Asia Pacific)
- Plenco 506 Black Heat Resistant Mineral Filled Phenolic Molding Compound (discontinued **)
- Kazanorgsintez 158-225 Film Grade Composition of High Density Polyethylene
- Styron MAGNUMâ„¢ 3904 Acrylonitrile Butadiene Styrene (ABS) Resin
- A. Schulman POLYFORT™ FPP 1477 Mineral Filled, General-Purpose Polypropylene
- DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 100 Gauge
- DuPont Performance Polymers Zytel® 103FHS BKB038 Nylon 66 (Unverified Data**)
- Aaron Industries AAROPRENE® GFIPP 2020 High Impact Glass Filled Polypropylene
- Parker Chomerics CHO-SHIELD® 598 A/B Silver-Epoxy Coating
Copyright © lookpolymers.com All Rights Reserved