SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* RAL22S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.700 % | 0.700 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm @Time 86400 sec |
0.019 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0192 cm/cm @Time 86400 sec |
0.0192 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0195 cm/cm @Time 86400 sec |
0.0195 in/in @Time 24.0 hour |
ISO 294 |
| 0.020 cm/cm @Time 86400 sec |
0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | ISO 527 |
| 81.0 MPa | 11700 psi | ASTM D638 | |
| Elongation at Break | 8.1 % | 8.1 % | ASTM D638 |
| 9.5 % | 9.5 % | ISO 527 | |
| Tensile Modulus | 3.44 GPa | 499 ksi | 50 mm/min; ASTM D638 |
| 3.50 GPa | 508 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| 117 MPa | 17000 psi | ISO 178 | |
| Flexural Modulus | 2.96 GPa | 429 ksi | ASTM D790 |
| 3.50 GPa | 508 ksi | ISO 178 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.55 | 0.55 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.46 | 0.46 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 73.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 82.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 82.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 248 °C @Thickness 3.20 mm |
478 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 198 °C @Thickness 3.20 mm |
388 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plansee MW20 Molybdenum-Tungsten
- Kraton® D1101 A (SBS) Liner Block Copolymer
- Samsung Cheil Industries Starex® SF-101H Expandable Polystyrene (EPS) FR
- ThyssenKrupp XAR® 600 Structural Steel
- Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled
- Ashley Polymers Ashlene® R528LW Nylon 66
- Bhansali Engineering Abstron SE32 FR IS15061 Flame Retardant ABS
Copyright © lookpolymers.com All Rights Reserved