SABIC Innovative Plastics Xenoy® X4870HH PC+PET
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X4870HH PC+PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xenoy X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. The X4870HH could be positioned for body panels, housings, medical device enclosures, outdoor sports equipment.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D 792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.14 % | 0.14 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % @Temperature 23.0 °C |
0.42 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 5.00 kg, Temperature 265 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 509 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 8.0 g/10 min @Load 5.00 kg, Temperature 266 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D 638 |
| 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 | |
| 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 | |
| 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D 638 |
| 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 | |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 | |
| 67.0 MPa | 9720 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
| 10 % | 10 % | 50 mm/min; ISO 527 | |
| 30 % | 30 % | Type I, 50 mm/min; ASTM D 638 | |
| 60 % | 60 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.3 % | 3.3 % | Type I, 50 mm/min; ASTM D 638 |
| 3.6 % | 3.6 % | 5 mm/min; ISO 527 | |
| 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D 638 | |
| 3.8 % | 3.8 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
| 4.60 GPa | 667 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| 104 MPa | 15100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 4.00 GPa | 580 ksi | 2 mm/min; ISO 178 |
| 4.25 GPa | 616 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.700 J/cm @Temperature -30.0 °C |
1.31 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.800 J/cm @Temperature 0.000 °C |
1.50 ft-lb/in @Temperature 32.0 °F |
ASTM D 256 | |
| 0.900 J/cm @Temperature 23.0 °C |
1.69 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 90.0 J | 66.4 ft-lb | Multiaxial Impact; ISO 6603 |
| 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| 60.0 J @Temperature -20.0 °C |
44.3 ft-lb @Temperature -4.00 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| Taber Abrasion, mg/1000 Cycles | 30 @Load 1.00 kg |
30 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 48.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
26.7 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
37.8 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 113 °C @Thickness 3.20 mm |
235 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ASTM D 1525 |
| 137 °C | 279 °F | Rate B/50; ISO 306 | |
| 139 °C | 282 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 8107 UV8D Butene LLDPE Rotational Molding Resin
- PolyOne Geon™ Vinyl Wire & Cable WJJC310L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Less Common Metals Erbium Vacuum Remelted Rare Earth Metal
- Lubriplate SFGO Ultra-22 PAO-Based Synthetic Food Machinery Grade Fluid
- LATI Latamid 6 H2 G/50 PA 6, 50% Glass Fiber Reinforced, Heat Stabilized
- Lucobit Lucofin® 1452 Polyolefin TPO Granules, Blue
- A. Schulman POLYBATCH™ Birch 60171U/4 Concentrate Based in LLDPE
- Denka TH-21 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene
- 3M 3W25X Protective UV Tape
- Arkema Group OREVAC® 18365 Maleic Anhydride Modified Polyethylene
Copyright © lookpolymers.com All Rights Reserved