Overview of materials for Polypropylene with Glass Fiber + Bead Filler

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with Glass Fiber + Bead Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene with Glass Fiber + Bead Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with Glass Fiber + Bead Filler". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.04 - 1.23 g/cc
0.0376 - 0.0444 lb/in³
Average value: 1.17 g/cc Grade Count:9
Filler Content 10.0 - 20.0 %
10.0 - 20.0 %
Average value: 15.0 % Grade Count:4
Water Absorption 0.0100 - 0.0200 %
0.0100 - 0.0200 %
Average value: 0.0120 % Grade Count:5
Linear Mold Shrinkage 0.00200 - 0.00900 cm/cm
0.00200 - 0.00900 in/in
Average value: 0.00491 cm/cm Grade Count:7
Melt Flow 2.50 - 10.0 g/10 min
2.50 - 10.0 g/10 min
Average value: 4.50 g/10 min Grade Count:4
Mechanical Properties Metric English Comments
Hardness, Rockwell R 85.0 - 120
85.0 - 120
Average value: 96.7 Grade Count:3
Tensile Strength, Ultimate 34.5 - 72.0 MPa
5000 - 10400 psi
Average value: 48.7 MPa Grade Count:7
18.0 - 40.0 MPa

@Temperature 60.0 - 120 °C
2610 - 5800 psi

@Temperature 140 - 248 °F
Average value: 29.3 MPa Grade Count:1
Elongation at Break 2.50 - 5.00 %
2.50 - 5.00 %
Average value: 3.43 % Grade Count:7
Modulus of Elasticity 3.59 - 5.60 GPa
520 - 812 ksi
Average value: 4.86 GPa Grade Count:7
Flexural Yield Strength 48.3 - 80.0 MPa
7000 - 11600 psi
Average value: 65.6 MPa Grade Count:7
Flexural Modulus 2.76 - 4.80 GPa
400 - 696 ksi
Average value: 3.88 GPa Grade Count:7
1.95 - 3.25 GPa

@Temperature 60.0 - 120 °C
283 - 471 ksi

@Temperature 140 - 248 °F
Average value: 2.59 GPa Grade Count:1
Izod Impact, Notched 0.374 - 0.800 J/cm
0.700 - 1.50 ft-lb/in
Average value: 0.544 J/cm Grade Count:7
0.400 - 0.450 J/cm

@Temperature -40.0 - -20.0 °C
0.749 - 0.843 ft-lb/in

@Temperature -40.0 - -4.00 °F
Average value: 0.425 J/cm Grade Count:1
Izod Impact, Unnotched 3.20 - 4.81 J/cm
6.00 - 9.00 ft-lb/in
Average value: 3.74 J/cm Grade Count:4
Charpy Impact Unnotched 1.70 - 1.70 J/cm²

@Temperature -40.0 - -20.0 °C
8.09 - 8.09 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 1.70 J/cm² Grade Count:1
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 132 - 163 °C
270 - 325 °F
Average value: 145 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 125 - 145 °C
257 - 293 °F
Average value: 135 °C Grade Count:9
Flammability, UL94 HB
HB
Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 - 1.00e+16 ohm-cm
1.00e+15 - 1.00e+16 ohm-cm
Average value: 8.20e+15 ohm-cm Grade Count:5
Processing Properties Metric English Comments
Processing Temperature 193 - 240 °C
380 - 464 °F
Average value: 212 °C Grade Count:5
Melt Temperature 195 - 302 °C
383 - 576 °F
Average value: 232 °C Grade Count:3
Mold Temperature 18.0 - 71.0 °C
64.4 - 160 °F
Average value: 46.9 °C Grade Count:8
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:4