- Plaskolite Optix® CA - 1000 E High Impact Grade Acrylic Resin
Plaskolite Optix® CA - 1000 E High Impact Grade Acrylic Resin
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded , Acrylic, Optical Grade, Molded |
| Manufacturer | Plaskolite |
| Trade Name | Optix® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plaskolite Optix® CA - 1000 E High Impact Grade Acrylic Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 1.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 44.9 MPa | 6510 psi | ASTM D-638 |
| Elongation at Break | 38 % | 38 % | ASTM D-638 |
| Modulus of Elasticity | 1.76 GPa | 255 ksi | ASTM D-638 |
| Flexural Strength | 61.3 MPa | 8890 psi | ASTM D-790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 6.35 mm |
1.20 ft-lb/in @Thickness 0.250 in |
ASTM D-256 |
| Gardner Impact | 6.33 J @Thickness 3.17 mm |
4.67 ft-lb @Thickness 0.125 in |
Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | ASTM D-696 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | UL-746 ABC |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D-648 |
| Vicat Softening Point | 108 °C | 227 °F | ASTM D-1525 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.8 % | <= 1.8 % | ASTM D-1003 |
| Transmission, Visible | 90.7 % | 90.7 % | ASTM D-1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 3-Year Weathering | Listed | SAE J 576 (AMECA) |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JC156HN Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics Lexan® CFR7431 PC COPOLYMER (Asia Pacific)
- Solvay Specialty Polymers FOMBLIN® Z60 PFPE Lubricant
- Stir SpA PVGUM 34 ATC UV (PVC)
- Borealis Borclear™ RE936CF Polypropylene Random Copolymer
- EMS-Grivory Grivory® CR 8 PA*
- Braskem S1522 LDPE Blow Molding Polyethylene
- Chevron Phillips K-Resin® BK13 Styrene-Butadiene Copolymer, Injection Molding Grade (discontinued **)
- Resistalloy International Fecralloy™ 134 Electrical Resistance Steel
Copyright © lookpolymers.com All Rights Reserved