SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xylex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HX7509HP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.12 % | 0.12 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 265 °C |
12 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Melt Index of Compound | 11 g/10 min @Load 2.16 kg, Temperature 265 °C |
11 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.0 MPa | 8990 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 133 % | 133 % | 50 mm/min; ISO 527 |
| 135 % | 135 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.8 % | 5.8 % | 50 mm/min; ISO 527 |
| 6.3 % | 6.3 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.14 GPa | 310 ksi | 50 mm/min; ASTM D638 |
| 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 8.50 J/cm | 15.9 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C |
1.31 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 77.0 J @Temperature 23.0 °C |
56.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| 104 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| 104 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 125 °C | 257 °F | Rate B/50; ISO 306 |
| 126 °C | 259 °F | Rate B/120; ISO 306 | |
| 126 °C | 259 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Gwent Electronic Materials C2050517D1 Carbon Graphite Ink
- LyondellBasell Petrothene® LP5100 High Density Polyethylene
- SABIC Innovative Plastics LNP THERMOCOMP PB006EQ PA 6 (Europe-Africa-Middle East)
- DuPont Appeel® LSR20D752 Lidding Sealant Resin
- Zotefoams Plastazote® LD24FMSV Low Density Polyethylene Foam, Flame Retarded
- Covestro Makrolon® 9125 Polycarbonate
- DuPont Performance Polymers Delrin® 100AF Acetal (POM) (Unverified Data**)
- Barlog Plastics KEBAFORM C 270 LS black POM Copolymer unreinforced, laser markable
- Arlon 51231R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
- ALM PA 601-CF Filled Nylon 12 Prototyping Polymer
Copyright © lookpolymers.com All Rights Reserved