SABIC Innovative Plastics Valox® V9500GW PET+PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® V9500GW PET+PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unfilled Flameretardant PET/PC blend for GWIT.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.70 %

@Temperature 23.0 °C
 0.70 %

@Temperature 73.4 °F
 ISO 62
Melt Flow 30 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 30 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.0 MPa
7830 psi
50 mm/min; ISO 527
Tensile Strength, Yield 52.0 MPa
7540 psi
50 mm/min; ISO 527
Elongation at Break 40 %
40 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 130 °C
266 °F
Rate B/50; ISO 306
140 °C
284 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 0.000 mm
 HB

@Thickness 0.000 in
 UL 94
HB

@Thickness 0.000 mm
 HB

@Thickness 0.000 in
 UL 94 by SABIC-IP
V-2

@Thickness 0.000 mm
 V-2

@Thickness 0.000 in
 UL 94 by SABIC-IP
V-2

@Thickness 0.000 mm
 V-2

@Thickness 0.000 in
 UL 94
V-1

@Thickness 0.000 mm
 V-1

@Thickness 0.000 in
 UL 94
V-1

@Thickness 0.000 mm
 V-1

@Thickness 0.000 in
 UL 94 by SABIC-IP
V-0

@Thickness 1.00 mm
 V-0

@Thickness 0.0394 in
 UL 94 by SABIC-IP
V-0

@Thickness 1.00 mm
 V-0

@Thickness 0.0394 in
 UL 94
Glow Wire Test 775 °C

@Thickness 1.00 mm
 1430 °F

@Thickness 0.0394 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
775 °C

@Thickness 2.00 mm
 1430 °F

@Thickness 0.0787 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
775 °C

@Thickness 3.00 mm
 1430 °F

@Thickness 0.118 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13