Barlog Plastics KEBATER BF110 PBT, 10% glass fiber reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATER |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATER BF110 PBT, 10% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT-GF10Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.18 % | 0.18 % | similar to ISO 62 test |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527-1 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | PBT-GF10 |
Users viewing this material also viewed the following:
- MRC Polymers SATRANâ„¢ 800R ABS Terpolymer, Reprocessed
- Tra-Con Tra-Bond 9349M Room Temperature Cure Flexible Epoxy Adhesive
- Tra-Con Tra-Duct 2979 Microelectronic Conductive Epoxy Adhesive
- Dow Tyrin® CM0836 Formulation
- Dow LDPE 5004I Low Density Polyethylene, Extrusion Coating Grade
- Dow SPECTRIM™ 50-S Reaction Moldable Polymer
- Alliance Polymers Viprene™ P85A-22U-NAT Thermoplastic Vulcanizate Elastomer
- Arkema Group Rilsan® BMN P20 D Nylon 11 (Conditioned)
- LNP Lubricomp® PDX-O-97635 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE Lubricant (discontinued **)&l
- Saint-Gobain Rulon® J Grade Bearing/Seal PTFE
Copyright © lookpolymers.com All Rights Reserved