BASF Polystyrol® 475 K Impact Grade Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 475 K Impact Grade Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Normal flowing, high-impact grade with particularly good creep strength.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
| Elongation at Break | 35 % | 35 % | |
| Elongation at Yield | 1.6 % | 1.6 % | |
| Tensile Modulus | 1.85 GPa | 268 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | |
| Vicat Softening Point | 90.0 °C | 194 °F | |
| Flammability, UL94 | HB @Thickness 3.05 mm |
HB @Thickness 0.120 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00040 @Frequency 1e+6 Hz |
0.00040 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 425 V | 425 V |
Users viewing this material also viewed the following:
- Polimeri Europa Intex® 132 Styrene - Butadiene Copolymer
- Solvay Specialty Polymers Halar® 9414 Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)&l
- Kinlead LSD12 Low Temperature Grade Heat Sealable Film (thickness: 20 µm)
- Shakespeare WN-102 diameter 0.5 mm Nylon 66 Monofilament
- SABIC Innovative Plastics LNP THERMOTUF VX00585 PA 66 (Asia Pacific)
- Trimay® Wear Plate T156 Iron-based Steel Overlay
- Dow Corning MOLYKOTE® G-00050 FG WHITE EP BEARING GREASE
- DuPont™ Nomex® 411 Paper, 15 mil Nominal Thickness
- Solvay Specialty Polymers Diofan® A 736 Polyvinylidene Chloride (PVDC) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved