SABIC Innovative Plastics Valox® EF4530 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® EF4530 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flow, 30% glass-reinforced, PBTP resin. Flame retardant.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.67 g/cc | 1.67 g/cc | ASTM D 792 |
| Viscosity | 400000 cP | 400000 cP | melt; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D 638 |
| Flexural Strength | 193 MPa | 28000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 11.54 GPa | 1674 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.27 J/cm @Temperature 23.0 °C |
8.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C @Thickness 6.40 mm |
428 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| UL RTI, Electrical | 140 °C | 284 °F | UL 746B |
| UL RTI, Mechanical with Impact | 125 °C | 257 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.760 mm |
V-0 @Thickness 0.0299 in |
UL 94 |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten, PLC code 7; ASTM D 495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | PLC code 3; UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | PLC code 0; UL 746A |
| High Amp Arc Ignition, HAI | 30 - 60 arcs | 30 - 60 arcs | surface, PLC code 2; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | PLC code 4; UL 746A |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 20 LS PA6, 20% glass beads, light stability
- Oceanchem Group Zinc Bromide
- Nitriflex N-8 NBR - Nitrile Rubber
- DuPont Performance Polymers Zytel® 101F BKB009 Nylon 66 (Unverified Data**)
- Crucible Steel MAXEL® Tooling Alloy Steel, AISI 4140 Modified
- Denka VINYKON R3105 PVC, R grade for hard extrusion
- BASF Neopolen® P 9235 0.07 g/cc Core density; Expanded Polypropylene (Europe)
- Polyram PlusTek RA320G5 Nylon 66 for Injection Molding, 25% Glass-Fiber Reinforced, Flame Retardant and High Stiffness
Copyright © lookpolymers.com All Rights Reserved