SABIC Innovative Plastics Valox® 830 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 830 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX 830 is a 30% glass fibre reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ASTM D229 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Viscosity | 208000 cP | 208000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on Tensile Bar; SABIC Method |
| 0.0020 - 0.010 cm/cm @Thickness 3.20 mm |
0.0020 - 0.010 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 265 °C |
16 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| 45 g/10 min @Load 5.00 kg, Temperature 265 °C |
45 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 | |
| Melt Index of Compound | 14 g/10 min @Load 2.16 kg, Temperature 265 °C |
14 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 23 g/10 min @Load 5.00 kg, Temperature 250 °C |
23 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 35 g/10 min @Load 5.00 kg, Temperature 265 °C |
35 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ISO 2039-2 |
| Hardness, H358/30 | 174 MPa | 25200 psi | ISO 2039-1 |
| Tensile Strength at Break | 140 MPa | 20300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 140 MPa | 20300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| 3.0 % | 3.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.5 GPa | 1520 ksi | 5 mm/min; ASTM D638 |
| 10.5 GPa | 1520 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 200 MPa | 29000 psi | 2 mm/min; ISO 178 |
| 205 MPa | 29700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 205 MPa | 29700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 215 MPa | 31200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 7.40 GPa | 1070 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.80 GPa | 1280 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| 0.900 J/cm @Temperature 0.000 °C |
1.69 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.900 J/cm @Temperature -30.0 °C |
1.69 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D4812 |
| 8.00 J/cm @Temperature -30.0 °C |
15.0 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature 0.000 °C |
4.28 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179/2C |
| 6.00 J/cm² | 28.6 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/2C | |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17, 1 kg; SABIC Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 3.6 @Frequency 100 Hz |
3.6 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
| 23.0 kV/mm @Thickness 1.60 mm |
584 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 23.0 kV/mm @Thickness 1.60 mm |
584 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 27.0 kV/mm @Thickness 0.800 mm |
686 kV/in @Thickness 0.0315 in |
in oil; ASTM D149 | |
| 27.0 kV/mm @Thickness 0.800 mm |
686 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.00080 @Frequency 50.0 - 60.0 Hz |
0.00080 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 | |
| 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Oxford Polymers PC/ABS 604i-FR PC/ABS, Flame retardant
- Magyar Aluminum ALOLT 60F Aluminum Hydroxide
- Heatbath/Park Partherm 350 Heat Transfer Salt
- Sylvin Technologies 8915-90 Natural PVC Extrusion Compound
- TIMET TIMETAL® Code 12 Titanium Alloy (ASTM Grade 12)
- A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
- DSM Arnitel® PL381 Injection Molding Grade Copolyester Elastomer (North America)
- 3M 6145 White Light Duty Reinforced Water Activated Tape
- Bulk Molding Compounds BMC A50-XHS High Strength Grade Molding Compound
- Tipco Tipcolene® IA 933 IN - 20% Talc/Mineral Reinforced Polypropylene Copolymer, High Flow, Stiffness & Impact Strength
Copyright © lookpolymers.com All Rights Reserved