SABIC Innovative Plastics Lexan® 3414R PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® 3414R PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40% GR, provides improved mechanical properties and UL94V-1 rated at 0.058"". Internal mold release added.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Density 1.522 g/cc
0.05499 lb/in³
ASTM D792
Water Absorption 0.12 %

@Time 86400 sec
 0.12 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.23 %
0.23 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0020 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 12.6 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 12.6 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 93
93
ASTM D785
Hardness, Rockwell R 119
119
ASTM D785
Tensile Strength at Break 158 MPa
22900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Flexural Yield Strength 186 MPa
27000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 9.65 GPa
1400 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.33 J/cm
2.49 ft-lb/in
ASTM D256
Izod Impact, Unnotched 12.81 J/cm
24.00 ft-lb/in
ASTM D4812
Tensile Impact Strength 67.0 kJ/m²
31.9 ft-lb/in²
Type S; ASTM D1822
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
ASTM D3029
Taber Abrasion, mg/1000 Cycles 32
32
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 16.2 µm/m-°C

@Temperature -40.0 - 95.0 °C
 9.00 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
Specific Heat Capacity 1.04 J/g-°C
0.249 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 154 °C

@Thickness 6.40 mm
 309 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 146 °C

@Thickness 6.40 mm
 295 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 165 °C
329 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 130 °C
266 °F
UL 746B
UL RTI, Mechanical with Impact 130 °C
266 °F
UL 746B
UL RTI, Mechanical without Impact 130 °C
266 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.11 mm
 V-1

@Thickness 0.0437 in
 UL 94
V-0

@Thickness 2.99 mm
 V-0

@Thickness 0.118 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+17 ohm-cm
>= 1.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.48

@Frequency 1.00e+6 Hz
 3.48

@Frequency 1.00e+6 Hz
 ASTM D150
3.53

@Frequency 50.0 - 60.0 Hz
 3.53

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Dielectric Strength 17.7 kV/mm

@Thickness 3.20 mm
 450 kV/in

@Thickness 0.126 in
 in air; ASTM D149
Dissipation Factor 0.0013

@Frequency 50.0 - 60.0 Hz
 0.0013

@Frequency 50.0 - 60.0 Hz
 ASTM D150
0.0067

@Frequency 1.00e+6 Hz
 0.0067

@Frequency 1.00e+6 Hz
 ASTM D150
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Specific Volume 0.65cm^3/g
ASTM D792