SABIC Innovative Plastics Valox® 8032UX PBT+PET (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 8032UX PBT+PET (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housings, door handles, mirror brackets.
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ASTM D792
Density 1.54 g/cc
0.0556 lb/in³
ISO 1183
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.16 %
0.16 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.010 cm/cm
0.0060 - 0.010 in/in
on Tensile Bar; SABIC Method
0.0060 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.010 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 21 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 21 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D1238
Melt Index of Compound 15 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ISO 2039-2
Hardness, H358/30 110 MPa
16000 psi
ISO 2039-1
Tensile Strength at Break 115 MPa
16700 psi
Type I, 5 mm/min; ASTM D638
145 MPa
21000 psi
5 mm/min; ISO 527
Tensile Strength, Yield 115 MPa
16700 psi
Type I, 5 mm/min; ASTM D638
145 MPa
21000 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.4 %
2.4 %
5 mm/min; ISO 527
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.4 %
2.4 %
5 mm/min; ISO 527
Tensile Modulus 9.50 GPa
1380 ksi
1 mm/min; ISO 527
9.95 GPa
1440 ksi
5 mm/min; ASTM D638
Flexural Strength 210 MPa
30500 psi
2 mm/min; ISO 178
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 8.45 GPa
1230 ksi
1.3 mm/min, 50 mm span; ASTM D790
8.50 GPa
1230 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.570 J/cm
1.07 ft-lb/in
ASTM D256
0.480 J/cm

@Temperature -30.0 °C
 0.899 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 4.80 J/cm
8.99 ft-lb/in
ASTM D4812
4.70 J/cm

@Temperature -30.0 °C
 8.81 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature 0.000 °C
 3.81 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*4; ISO 180/1U
40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 8.00 J

@Temperature 23.0 °C
 5.90 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Taber Abrasion, mg/1000 Cycles 30
30
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 22.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 12.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
25.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
81.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 45.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
423 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
208 °C

@Thickness 3.20 mm
 406 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
190 °C

@Thickness 3.20 mm
 374 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 202 °C
396 °F
Rate B/50; ISO 306
203 °C
397 °F
Rate B/50; ASTM D1525
204 °C
399 °F
Rate B/120; ISO 306
220 °C
428 °F
Rate A/50; ISO 306
221 °C
430 °F
Rate A/50; ASTM D1525
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
3.3

@Frequency 50.0 - 60.0 Hz
 3.3

@Frequency 50.0 - 60.0 Hz
 IEC 60250
3.6

@Frequency 100 Hz
 3.6

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 15.0 kV/mm

@Thickness 3.20 mm
 381 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
23.0 kV/mm

@Thickness 1.60 mm
 584 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
27.0 kV/mm

@Thickness 0.800 mm
 686 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.00080

@Frequency 50.0 - 60.0 Hz
 0.00080

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.013

@Frequency 1.00e+6 Hz
 0.013

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 300 V
300 V
IEC 60112
250 - 400 V
250 - 400 V
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2