SABIC Innovative Plastics Xylex X8303CL PC+POLYESTER

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xylex X8303CL PC+POLYESTER.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+ POLYESTER, Transparent, Low processing Temperature, High flow with excellent impact, UV stabilized, OQ quality. For In Mold Decoration /Labeling.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %

@Temperature 23.0 °C
 0.50 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 27 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 27 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
30 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 30 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
50 mm/min; ISO 527
44.0 MPa
6380 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D 638
48.0 MPa
6960 psi
50 mm/min; ISO 527
Elongation at Break 140 %
140 %
Type I, 50 mm/min; ASTM D 638
140 %
140 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D 638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 1.68 GPa
244 ksi
5 mm/min; ASTM D 638
1.69 GPa
245 ksi
1 mm/min; ISO 527
Flexural Strength 72.0 MPa
10400 psi
2 mm/min; ISO 178
Flexural Yield Strength 72.0 MPa
10400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 1.62 GPa
235 ksi
1.3 mm/min, 50 mm span; ASTM D 790
1.72 GPa
249 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.00 J/cm

@Temperature -30.0 °C
 1.87 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
10.0 J/cm

@Temperature 23.0 °C
 18.7 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.40 J/cm²

@Temperature 23.0 °C
 6.66 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 65.0 J

@Temperature 23.0 °C
 47.9 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
92.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 51.1 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
98.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 54.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C

@Thickness 3.20 mm
 198 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
80.0 °C

@Thickness 3.20 mm
 176 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 98.0 °C
208 °F
Rate B/50; ASTM D 1525
100 °C
212 °F
Rate B/50; ISO 306
100 °C
212 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified