SABIC Innovative Plastics Ultem HU2410 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem HU2410 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications.
Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ASTM D 792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Water Absorption | 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
ASTM D 570 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 23°C / 50% RH; ISO 62 |
| 0.90 % @Temperature 23.0 °C |
0.90 % @Temperature 73.4 °F |
ASTM D 570 | |
| Water Absorption at Saturation | 0.80 % @Temperature 23.0 °C |
0.80 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.2 g/10 min @Load 6.60 kg, Temperature 337 °C |
5.2 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| 11 g/10 min @Load 5.00 kg, Temperature 220 °C |
11 g/10 min @Load 11.0 lb, Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 179 MPa | 26000 psi | Type I, 5 mm/min; ASTM D 638 |
| 180 MPa | 26100 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 180 MPa | 26100 psi | 5 mm/min; ISO 527 |
| 186 MPa | 27000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 11.5 GPa | 1670 ksi | 1 mm/min; ISO 527 |
| 11.72 GPa | 1700 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 240 MPa | 34800 psi | 2 mm/min; ISO 178 |
| 254 MPa | 36800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 |
| 11.43 GPa | 1658 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 1.12 J/cm @Temperature 23.0 °C |
2.10 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 1.14 J/cm @Temperature -30.0 °C |
2.14 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 4.27 J/cm @Temperature 23.0 °C |
8.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 18.0 J @Temperature 23.0 °C |
13.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.4 µm/m-°C @Temperature -20.0 - 150 °C |
8.00 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| 15.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.33 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 214 °C | 417 °F | Rate B/50; ISO 306 |
| 215 °C | 419 °F | Rate B/120; ISO 306 | |
| 234 °C | 453 °F | Rate B/50; ASTM D 1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Oxygen Index | 54 % | 54 % | LOI; ASTM D 2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.50e+16 ohm-cm | 1.50e+16 ohm-cm | ASTM D 257 |
| Dielectric Constant | 3.7 @Frequency 1000 Hz |
3.7 @Frequency 1000 Hz |
ASTM D 150 |
| Dielectric Strength | 24.0 kV/mm @Thickness 1.60 mm |
610 kV/in @Thickness 0.0630 in |
in oil; ASTM D 149 |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz |
0.0020 @Frequency 1000 Hz |
ASTM D 150 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL 1401 Conductive Elastomer
- Lucent Polymers GPP-330 Polypropylene, 30% Glass Fiber Reinforced, Chemically Coupled, Impact Modified
- A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene
- A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT
- Dow C759-21NA Polypropylene Impact Copolymer Resin
- DuPont Teijin Films Melinex® 437 Polyester Film, 200 Gauge
- Abatron AboCast 8103-26 High-Performance Dielectric Epoxy
- ExxonMobil Santoprene® 8271-80HT Thermoplastic Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved