- Lubrizol Pellethane® 2363-90A Thermoplastic Polyurethane Elastomer
Lubrizol Pellethane® 2363-90A Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Pellethane® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Pellethane® 2363-90A Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 30 g/10 min @Load 1.20 kg, Temperature 224 °C |
30 g/10 min @Load 2.65 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | ASTM D2240 |
| Tensile Strength, Ultimate | 40.3 MPa | 5850 psi | ASTM D412 |
| Elongation at Break | 500 % | 500 % | ASTM D412 |
| 50% Modulus | 0.00830 GPa | 1.20 ksi | ASTM D412 |
| 100% Modulus | 0.0117 GPa | 1.70 ksi | ASTM D412 |
| 300% Modulus | 0.0207 GPa | 3.00 ksi | ASTM D412 |
| Flexural Modulus | 0.0758 GPa | 11.0 ksi | ASTM D790 |
| Tear Strength | 100 kN/m | 571 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 25 % @Temperature 25.0 °C, Time 79200 sec |
25 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395, Method B |
| 30 % @Temperature 70.0 °C, Time 79200 sec |
30 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395, Method B | |
| Tensile Set | 30 % | 30 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 157 µm/m-°C @Temperature -80.0 - -30.0 °C |
87.2 µin/in-°F @Temperature -112 - -22.0 °F |
ASTM D696 |
| Vicat Softening Point | 110 °C | 230 °F | 120°C.hr, 9.8N; ASTM D1525 |
| Glass Transition Temp, Tg | -30.0 °C | -22.0 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 221 °C | 399 - 430 °F | Molding |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 88.0 - 104 °C | 190 - 219 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- RheTech Products T40P100-01 40% Talc Reinforced Polypropylene, Black
- Polimeri Europa Extir® CM Galileo Europa 5 AE Expandable Polystyrene - Continuous Mass
- Techmer ES Plaslube® J-50/10/SI/2 Polycarbonate, 10% GFR, 2% Silicone
- A. Schulman PAPERMATCH® H-3818 Specialty Masterbatch
- Diamond Polymers SAN 268 Styrene Acrylonitrile, Transparent Engineering Thermoplastic
- 3M Scotch-Weld™ TL90 Threadlocker Anaerobic Adhesive
- Arkema Group KYNAR FLEX® 2850-04 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
- Lubrizol ESTANE® 58271 Ester Based Thermoplastic Polyurethane
- 3M AC-250 B-1/6 Aerospace Sealant
Copyright © lookpolymers.com All Rights Reserved