SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed.
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D792
Density 1.28 g/cc
0.0462 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.36 %
0.36 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 43 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 43 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Melt Index of Compound 56 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 56 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
5 mm/min; ISO 527
85.0 MPa
12300 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 98.0 MPa
14200 psi
5 mm/min; ISO 527
103 MPa
14900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 80 %
80 %
Type I, 5 mm/min; ASTM D638
80 %
80 %
5 mm/min; ISO 527
Elongation at Yield 7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
7.0 %
7.0 %
5 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527
3.21 GPa
466 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 135 MPa
19600 psi
2 mm/min; ISO 178
145 MPa
21000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
2 mm/min; ISO 178
3.32 GPa
482 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
0.350 J/cm

@Temperature -30.0 °C
 0.656 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 2.00 kJ/m²
0.952 ft-lb/in²
80*10*4; ISO 180/1A
2.00 kJ/m²

@Temperature -30.0 °C
 0.952 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 48.0 J

@Temperature 23.0 °C
 35.4 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.0 µm/m-°C

@Temperature 23.0 - 150 °C
 30.6 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
60.0 µm/m-°C

@Temperature -40.0 - 150 °C
 33.3 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature 23.0 - 150 °C
 30.6 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
60.0 µm/m-°C

@Temperature -40.0 - 150 °C
 33.3 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 168 °C
334 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
173 °C

@Thickness 3.20 mm
 343 °F

@Thickness 0.126 in
 unannealed; ASTM D648
178 °C

@Thickness 6.40 mm
 352 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 192 °C
378 °F
Rate B/50; ASTM D1525
192 °C
378 °F
Rate B/50; ISO 306
195 °C
383 °F
Rate B/120; ISO 306
Glass Transition Temp, Tg 200 °C
392 °F
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified