- LTL Color Compounds ColorFast® FRPA100X Polycarbonate-ABS Alloy
LTL Color Compounds ColorFast® FRPA100X Polycarbonate-ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRPA100X Polycarbonate-ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
V-0 rated polycarbonate-ABS alloy, excellent toughness and light stabilityAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | 0.125; ASTM D955 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 260 °C |
14 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 55.8 MPa | 8100 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 90 % | 90 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 95.1 MPa | 13800 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Temperature 22.8 °C |
12.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 254 °C | 410 - 490 °F | |
| Middle Barrel Temperature | 216 - 260 °C | 420 - 500 °F | |
| Front Barrel Temperature | 227 - 274 °C | 440 - 525 °F | |
| Nozzle Temperature | 232 - 274 °C | 450 - 525 °F | |
| Melt Temperature | 232 - 274 °C | 450 - 525 °F | |
| Mold Temperature | 60.0 - 82.2 °C | 140 - 180 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 60 % | 30 - 60 % | |
| Vent Depth | 0.00381 - 0.00762 cm | 0.00150 - 0.00300 in | |
| Screw Speed | 30 - 75 rpm | 30 - 75 rpm |
Users viewing this material also viewed the following:
- MV Labs CA200 CaBr2·xH2O Calcium bromide hydrate
- Eastman Eastar GN005 Copolyester, Natural (discontinued **)
- Inno-Comp INNOPOL® CS 1-5830 30% Glass-Fiber-Filled Polypropylene Homopolymer
- Lord Adhesives 4 No-Mix Accelerator for 200/500 Series
- Industeel NUCL 18.10 B4 Natural Boron (Min 1% wt) Alloyed 304 Stainless Steel
- SABIC Innovative Plastics LNP Thermocomp DF0066P PC
- Elmer's Products Aron Alpha® 253TX Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- Bulk Molding Compounds BMC 2274 Mineral Filled, Glass Reinforced Polyester
- Asahi Kasei Xyron® AT610 Modified Polyphenylene Ether
- Fainplast Compounds GS 60 Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved