SABIC Innovative Plastics ULTEM 2400 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 2400 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. WRAS certification in recognized colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ASTM D792 |
| Water Absorption | 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 4.2 g/10 min @Load 6.60 kg, Temperature 337 °C |
4.2 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 114 | 114 | ASTM D785 |
| Tensile Strength at Break | 179 MPa | 26000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 11.72 GPa | 1700 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 241 MPa | 35000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 11.72 GPa | 1700 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| 4.80 J/cm @Thickness 3.20 mm |
8.99 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Unnotched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.4 µm/m-°C @Temperature -20.0 - 150 °C |
8.00 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 234 °C | 453 °F | Rate B/50; ASTM D1525 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.250 mm |
V-0 @Thickness 0.00984 in |
UL 94 |
| Oxygen Index | 54 % | 54 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.50e+16 ohm-cm | 1.50e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1000 Hz |
3.7 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 24.0 kV/mm @Thickness 1.60 mm |
610 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz |
0.0020 @Frequency 1000 Hz |
ASTM D150 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 0.00 - 100 V | 0.00 - 100 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| NBS Smoke Density, Flaming, Ds 4 min | 1 | ASTM E 662 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF5020 HC Polypropylene Homopolymer, Glass Fiber Reinforced
- PolyOne Geon™ Vinyl Flexible R235AE White 1875 Polyvinyl Chloride, Flexible (PVC, Flexible)
- H.C. Starck Amperit® 539.054 Agglomerated, Sintered Tungsten Carbide-Tungsten Boride-Cobalt-Chromium (WC-WB-Co-Cr) 60-30-5-5
- Teknor Apex Fireguard® 910-A10-NL2 Polyvinyl Chloride, Flexible
- Plenco 3356 Phenolic, Granular, Compression Molded
- Unitika elitel UE3231 Polyester, Flake
- Lubrizol Estane® ALR G500 Water Absorbent Thermoplastic Polyurethane
- 3M FS022 Clear Polystyrene Label Products
- A. Schulman ComAlloy Hiloy® 431 Glass Reinforced, PBT Alloy
Copyright © lookpolymers.com All Rights Reserved