Resinoid 1312 Phenolic Molding, Glass Reinforced

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer	Resinoid
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Resinoid 1312 Phenolic Molding, Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance

Physical Properties	Metric	English	Comments
Density	1.90 g/cc	0.0686 lb/in³	ASTM D792A
Water Absorption	0.10 %	0.10 %	24 hours R.T. ASTM D570
Linear Mold Shrinkage	0.0035 cm/cm	0.0035 in/in	Positive Mold; ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	48.0 MPa	6960 psi	ASTM D651
Flexural Strength	84.0 MPa	12200 psi	ASTM D790
Flexural Modulus	14.0 GPa	2030 ksi	ASTM D790
Compressive Strength	170 MPa	24700 psi	ASTM D695
Izod Impact, Notched	0.446 J/cm	0.836 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English
Maximum Service Temperature, Air	150 °C	302 °F
UL RTI, Electrical	150 °C	302 °F
UL RTI, Mechanical with Impact	150 °C	302 °F
UL RTI, Mechanical without Impact	150 °C	302 °F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	250 - 399 V @Thickness 3.05 mm	250 - 399 V @Thickness 0.120 in	UL PLC 2 (250-399 V)
Hot Wire Ignition, HWI	>= 120 sec @Thickness 3.05 mm	>= 120 sec @Thickness 0.120 in	UL PLC 0; UL PLC 0
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 3.05 mm	>= 120 arcs @Thickness 0.120 in	UL PLC 0; UL PLC 0
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min @Thickness 3.05 mm	0.000 - 0.394 in/min @Thickness 0.120 in	UL PLC 0 (0-10 mm/min)

Processing Properties	Metric	English	Comments
Mold Temperature	155 - 180 °C	311 - 356 °F