Special Metals INCONEL® Alloy 600
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® Alloy 600.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-chromium alloy with good oxidation resistance at high temperatures and resistance to chloride-ion stress-corrosion cracking, corrosion by high-purity water, and caustic corrosion. Used for furnace components, in chemical and food processing, in nuclear engineering, and for sparking electrodes. Standard product forms are round, hexagon, extruded section, flats, forging stock, pipe, tube, plate, sheet, strip, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.47 g/cc | 0.306 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 655 MPa | 95000 psi | Annealed |
| 550 MPa @Temperature 550 °C |
79800 psi @Temperature 1020 °F |
Annealed prior to test | |
| Tensile Strength, Yield | 310 MPa | 45000 psi | Annealed |
| 180 MPa @Temperature 550 °C |
26100 psi @Temperature 1020 °F |
Annealed prior to test | |
| Elongation at Break | 45 % | 45 % | Annealed prior to test. |
| 42 % @Temperature 550 °C |
42 % @Temperature 1020 °F |
Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 100 °C |
7.39 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Thermal Conductivity | 14.9 W/m-K | 103 BTU-in/hr-ft²-°F | |
| Melting Point | 1354 - 1413 °C | 2469 - 2575 °F | |
| Solidus | 1354 °C | 2469 °F | |
| Liquidus | 1413 °C | 2575 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.15 % | <= 0.15 % | |
| Chromium, Cr | 14 - 17 % | 14 - 17 % | |
| Copper, Cu | <= 0.50 % | <= 0.50 % | |
| Iron, Fe | 6.0 - 10 % | 6.0 - 10 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Nickel, Ni | >= 72 % | >= 72 % | Including Cobalt |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000103 ohm-cm | 0.000103 ohm-cm | |
| Magnetic Permeability | 1.01 | 1.01 | at 200 oersted (15.9 kA/m) |
| Curie Temperature | -194 °C | -317 °F |
Users viewing this material also viewed the following:
- Nabaltec GRANALOX® NM 9620 Ceramic Bodies
- Polimeri Europa Extir® PD D 2000 AE Expandable Polystyrene, Fast Molding Flame Retardant (discontinued **)<
- Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F)
- Solvay TECHNYL® A 221 PA66, Conditioned
- Teknor Apex Tekbond® TB 1339A Thermoplastic Elastomer
- Unipetrol PP MONSTEN® GH 001 Polypropylene Homopolymer
- Denka LCS Z1075 Thermoplastic Elastomer, Extrusion grade (general)
- 3M Jet-melt™ 3731 Polyolefin Bonding Adhesive
Copyright © lookpolymers.com All Rights Reserved