- SABIC Innovative Plastics NORYL V095 PPE+PS (Europe-Africa-Middle East)
SABIC Innovative Plastics NORYL V095 PPE+PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL V095 PPE+PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* V095 resin is a modified PPE-PS blend that exhibits an excellent balance of non chlorinate, non brominate flame retardance, medium heat/high flow and low specific gravity for light weight parts. Noryl V095 is available in custom colors and may be an excellent material candidate for applications requiring light weight parts, good flame performance and excellent processability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.070 % | 0.070 % | ISO 62 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC Method |
| Melt Flow | 16.2 g/10 min @Load 3.80 kg, Temperature 200 °C |
16.2 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D1238 |
| Melt Index of Compound | 12 g/10 min @Load 1.20 kg, Temperature 280 °C |
12 g/10 min @Load 2.65 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 26 g/10 min @Load 2.16 kg, Temperature 280 °C |
26 g/10 min @Load 4.76 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 12 % | 12 % | Type I, 50 mm/min; ASTM D638 |
| 13 % | 13 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 3.2 % | 3.2 % | 50 mm/min; ISO 527 |
| 3.5 % | 3.5 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.58 GPa | 374 ksi | 50 mm/min; ASTM D638 |
| 2.61 GPa | 379 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| 2.58 GPa | 374 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 100 °C | 212 °F | Rate B/50; ISO 306 |
| 101 °C | 214 °F | Rate B/120; ISO 306 | |
| 101 °C | 214 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Oxygen Index | 31 % | 31 % | ISO 4589 |
| Glow Wire Test | 700 °C | 1290 °F | IEC 60695-2-13 |
| 700 °C | 1290 °F | IEC 60695-2-13 | |
| 700 °C | 1290 °F | IEC 60695-2-13 | |
| 850 °C @Thickness 3.00 mm |
1560 °F @Thickness 0.118 in |
IEC 60695-2-12 | |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.90e+16 ohm-cm | 1.90e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.90e+17 ohm | 1.90e+17 ohm | ASTM D257 |
| 1.90e+17 ohm | 1.90e+17 ohm | ROA; IEC 60093 | |
| Dielectric Constant | 2.9 @Frequency 1000 Hz |
2.9 @Frequency 1000 Hz |
IEC 60250 |
| Dissipation Factor | 0.0080 @Frequency 1000 Hz |
0.0080 @Frequency 1000 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Impact Modified 411 HS Nylon 6/6
- Kennametal Stellite Stellite® 20 Cobalt Alloy
- Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F)
- LG Chemical LUPOY GN1002FS PC, Halogen Free, Flame Retardant, High Impact
- Shakespeare WonderThread® SN-38 High tenacity TEX# 14 Nylon Industrial Sewing Thread
- Trelleborg B574 Nitrile Rubber
- EMS-Grivory Grivory® BG-30 FC PA6-GF30
- 3M 5188 (Clear) Polyethylene Protective Tapes
- DSM Stanyl® 46HF5050 Nylon 46-50% Glass Reinforced (European and Asian Grade) (Dry)
Copyright © lookpolymers.com All Rights Reserved