LATI Latan 23UV POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer LATI
Trade Name Latan
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latan 23UV POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyoxymethylene (POM). UV stabilized. Low viscosity. Very good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
Linear Mold Shrinkage, Flow 0.0195 - 0.023 cm/cm
0.0195 - 0.023 in/in
Linear Mold Shrinkage, Transverse 0.020 - 0.0225 cm/cm
0.020 - 0.0225 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
Elongation at Break 40 %

@Temperature 23.0 °C
40 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
>= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
>= 100 %

@Temperature 194 °F
Elongation at Yield 10 %
10 %
Tensile Modulus 1.10 GPa

@Temperature 90.0 °C
160 ksi

@Temperature 194 °F
1.60 GPa

@Temperature 60.0 °C
232 ksi

@Temperature 140 °F
2.70 GPa

@Temperature 23.0 °C
392 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 75.0 °C
167 °F
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Vicat Softening Point 150 °C

@Load 5.00 kg
302 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 175 - 200 °C
347 - 392 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa