SABIC Innovative Plastics NORYL V03505 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL V03505 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* V03505 is a 35% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 2.0 mm. Noryl V03505 is may be an excellent material candidate for application requiring low warpage and flame resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 49 g/10 min @Load 5.00 kg, Temperature 300 °C |
49 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 15 g/10 min @Load 3.80 kg, Temperature 280 °C |
15 g/10 min @Load 8.38 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 24 g/10 min @Load 5.00 kg, Temperature 280 °C |
24 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 147 MPa | 21300 psi | ISO 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 59.0 MPa | 8560 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 |
| 5.00 GPa | 725 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.30 GPa | 624 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.70 GPa | 682 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| 0.350 J/cm @Temperature -30.0 °C |
0.656 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| 24.0 kJ/m² @Temperature -30.0 °C |
11.4 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
22.2 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 105 °C | <= 221 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 110 °C | 230 °F | Rate B/50; ISO 306 |
| 115 °C | 239 °F | Rate B/50; ASTM D1525 | |
| 120 °C | 248 °F | Rate A/50; ISO 306 | |
| 120 °C | 248 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
UL 94 | |
| Oxygen Index | 34 % | 34 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.2 @Frequency 50.0 - 60.0 Hz |
3.2 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 26.0 kV/mm @Thickness 1.60 mm |
660 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 33.0 kV/mm @Thickness 0.800 mm |
838 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0060 @Frequency 50.0 - 60.0 Hz |
0.0060 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- RheTech Products G40P100-04UV 40% Glass Fiber Reinforced Polypropylene, UV Stabilized, White
- Sibur ABS 2802 Extrusion Grade ABS Plastic
- Silberline Sparkle Silvex® Premier 890-20-C
- Styron Magnumâ„¢ 358HP ABS, High Heat
- A. Schulman POLYTROPE™ TPP 403 Blow Molding Grade Olefinic Thermoplastic Elastomer
- TIMCAL TIMREX® SFG15 Primary Synthetic Graphite
- Fainplast Compounds HL 90/4 Flexible PVC, Insulation for High Temperatures
- Dynasol Calprene® 411 Thermoplastic Rubber SBS Dry
- SABIC Innovative Plastics Noryl FXN119LG PPE+HIPS (Europe-Africa-Middle East)
- ExxonMobil Santoprene® 201-55W175 Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved