SABIC Innovative Plastics NORYL N1150 PPE+PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL N1150 PPE+PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* N1150 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 0.75 mm with a specific density of 1.11 g/cm^3. Noryl* 1150 may be an excellent material candidate for applications requiring electrically insulating properties, low moisture absorption, low warpage, and thin wall flame resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.070 % | 0.070 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 280 °C |
15 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 15 g/10 min @Load 5.00 kg, Temperature 280 °C |
15 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | 50 mm/min; ISO 527 |
| 75.0 MPa | 10900 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
| 8.0 % | 8.0 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527 |
| 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.65 GPa | 384 ksi | 1 mm/min; ISO 527 |
| 2.70 GPa | 392 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
| 117 MPa | 17000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 |
| 3.05 GPa | 442 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| 0.650 J/cm @Temperature -30.0 °C |
1.22 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 40.0 J @Temperature 23.0 °C |
29.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 54.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 57.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 57.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ASTM D1525 |
| 130 °C | 266 °F | Rate B/50; ISO 306 | |
| 132 °C | 270 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 | |
| Oxygen Index | 38 % | 38 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+16 ohm-cm | 5.00e+16 ohm-cm | ASTM D257 |
| 5.00e+16 ohm-cm | 5.00e+16 ohm-cm | IEC 60093 | |
| Surface Resistance | 2.00e+16 ohm | 2.00e+16 ohm | ASTM D257 |
| 2.00e+16 ohm | 2.00e+16 ohm | ROA; IEC 60093 | |
| Dielectric Constant | 2.6 @Frequency 1.00e+6 Hz |
2.6 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 2.6 @Frequency 1.00e+6 Hz |
2.6 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 |
| 250 - 400 V | 250 - 400 V | UL 746A |
Users viewing this material also viewed the following:
- Quantum PEEK 30% Carbon Filled
- Mitsubishi Iupilon® H2000R 23 MFI Polycarbonate With Release
- Karina 802-06/77-Y-BZ Blue PVC Compound
- Shandong Rike Chemical HELIâ„¢ HL-90 PVC Processing Aid Series (PA)
- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work
- SIDPEC EGYPTENE® HD 3840 EA MDPE Wire and Cable Grade
- A. Schulman POLYFORT™ FPP 1640 Glass Reinforced, Mineral Fortified Homopolymer Polypropylene
- Alliance BIS-82 Bonded (Composite) Magnetic Material
- Fainplast Compounds KLT 93 Flexible PVC, Insulation Transparent Cables Lead Free
Copyright © lookpolymers.com All Rights Reserved