PolyOne Edgetek® RA-15GF/000 Polyethersulfone, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® RA-15GF/000 Polyethersulfone, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedUL 94 V0UL 94 (CTI Testing)PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 93.1 MPa | 13500 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.48 GPa | 650 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Annealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 349 - 388 °C | 660 - 730 °F | Molding |
| Mold Temperature | 93.3 - 163 °C | 200 - 325 °F | |
| Drying Temperature | 149 °C | 300 °F | 2 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Nye Lubricants 790G-MS (RL) Synthetic Oil
- Polymax® Maxelast® P2625 TPE, PP Overmold or Standalone use
- MarkeTech Silicon Single Crystal Semiconductor Wafer, n-type, Arsenic Doped, Czochralski-LED Grown
- Sibur SKI-3 1st Grade, 3rd Group Isoprene Rubber (IR)
- Samsung Cheil Industries Infino® LF-1025 PC, Unreinforced Anti-Abrasion
- A. Schulman CP851 High Flow, Injection Molding Grade
- DuPont Performance Polymers VESPEL TP-8169 Polyimide
- ExxonMobil 150 Mobil DTE PM Ashless
- Dow LDPE 683I Low Density Polyethylene, Film Grade
- 3M 3W55Z Protective UV Tape
Copyright © lookpolymers.com All Rights Reserved