A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionPolyfort® FPP 1006S is a 20% talc filled homopolymer polypropylene compound formulated with an internal mold release. Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Melt Flow 10 g/10 min
10 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Flexural Modulus 2.275 GPa
330.0 ksi
ASTM D790
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 125 °C
257 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 71.0 °C
160 °F
ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness 0.780 mm
 149 °F

@Thickness 0.0307 in
 UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.780 mm
 149 °F

@Thickness 0.0307 in
 UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.780 mm
 149 °F

@Thickness 0.0307 in
 UL 746
Flammability, UL94 HB

@Thickness 0.780 mm
 HB

@Thickness 0.0307 in