SABIC Innovative Plastics NORYL GTX GTX830 PPE+PA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX830 PPE+PA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL GTX830 a 30% glass reinforced grade which offers an excellent combination of chemical/heat resistance in combination with stiffness.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.09 % | 1.09 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 3.1 % | 3.1 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 110 MPa | 16000 psi | ISO 2039-1 |
| Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.20 GPa | 899 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| 45.0 kJ/m² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/2C |
| 0.700 J/cm² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | ISO 8302 |
| Vicat Softening Point | 220 °C | 428 °F | Rate B/50; ISO 306 |
| 220 °C | 428 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 29 % | 29 % | ISO 4589 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF50 - PP Homopolymer Polypropylene, 50% Long Glass Fiber Reinforced
- IRPC Polimaxx Porene KU650 Acrylonitrile Butadiene Styrene
- Mikro-Technik Reproflon G25 PTFE
- Shandong Rike Chemical HELIâ„¢ HL-740 Weather-resistance Acrylic Impact Modifier (AIM)
- SABIC Innovative Plastics LNP THERMOCOMP AX05466H ABS (Asia Pacific)
- A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene
- ExxonMobil LDPE LD 615BA Low Density Polyethylene Resin (European Grade)
- Dow Nordel® IP 4520 General Purpose Compound
- Aclo Accutech Polypropylene Homopolymer HP0334G10M20CL Glass/Mineral Reinforced Coupled
Copyright © lookpolymers.com All Rights Reserved