SABIC Innovative Plastics Noryl GTX LMX171 PPO/PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GTX LMX171 PPO/PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl LMX171 is a PPO/PBT blend including conductive agent with a balanced heat/impact property profile. Noryl LMX differentiate from Noryl GTX by a lower moisture uptake (0.15%).This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Viscosity | 200000 cP @Temperature 282 °C |
200000 cP @Temperature 540 °F |
melt; 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.022 - 0.026 cm/cm | 0.022 - 0.026 in/in | on tensile bar; SABIC Method |
| Melt Flow | 25 g/10 min @Load 10.0 kg, Temperature 280 °C |
25 g/10 min @Load 22.0 lb, Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 25 % | 25 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 70.0 J | 51.6 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C @Temperature 23.0 - 60.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 23.0 - 60.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Vicat Softening Point | 163 °C | 325 °F | Rate B/50; ISO 306 |
| 163 °C | 325 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Fibre Glast Duratec 1040 Clear Hi-Gloss Gel Coat Additive
- Lubrizol Advanced Materials PEARLBOND® 501 Linear Thermoplastic Polyurethane
- Sharadaa Ceramics Blankets
- SK Chemicals SKYTHANE® S385A Polyester Based Thermoplastic Polyurethane Elastomer
- TIMCAL TIMREX® KS44 Primary Synthetic Graphite
- Hexcel® HexPly® ES/EH 84 120°C Curing Epoxy Matrix
- ExxonMobil HDPE HD 8760.29 High Density Polyethylene Resin
- A. Schulman ComAlloy Comtuf® 101 Polypropylene, Mineral Reinforced, Impact Modified
- Polyram RamOfin PPC104 Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved