PolyOne Versaflex™ FFC 2882-87 Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Versaflex™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Versaflex™ FFC 2882-87 Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Versaflex™ FFC 2882-87 is designed to pass several fatty food extraction conditions identified in EU Directive 2002/72/EC, FDA 21 CFR 177.2600, and GB 4806.1-94. Versaflex™ FFC 2882-87 will also overmold and co-extrude to polypropylene.Rear: 380-400F Center: 390-420F Front: 400-440F Screw: 100-500rpmColor concentrates based on polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (LDPE) are most suitable for coloring Versaflex™ FFC 2882-87. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25-40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by the use of precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials. Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Regrind levels up to 20% can be used with Versaflex™ FFC 2882-87 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Versaflex™ FFC 2882-87 has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer. Drying is not Required Injection Speed: 1 to 3 in/sec 1st Stage - Boost Pressure: 500 to 700 psi 2nd Stage - Hold Pressure: 10 to 30% of Boost Hold Time (Thick Part): 2 to 4 sec Hold Time (Thin Part): 1 to 2 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 0.878 g/cc
0.878 g/cc
ASTM D792
Viscosity 34800 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
34800 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
Linear Mold Shrinkage, Flow 0.0090 - 0.015 cm/cm
0.0090 - 0.015 in/in
Injection Molded; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore A 88
88
10 sec; ASTM D2240
Tensile Strength at Break 9.03 MPa

@Temperature 23.0 °C
1310 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 7.25 MPa

@Strain 100 %,
Temperature 23.0 °C
1050 psi

@Strain 100 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
7.65 MPa

@Strain 300 %,
Temperature 23.0 °C
1110 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 700 %

@Temperature 23.0 °C
700 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Processing Properties Metric English Comments
Rear Barrel Temperature 193 - 204 °C
379 - 399 °F
Middle Barrel Temperature 199 - 216 °C
390 - 421 °F
Front Barrel Temperature 204 - 227 °C
399 - 441 °F
Nozzle Temperature 210 - 238 °C
410 - 460 °F
Die Temperature 216 - 238 °C
421 - 460 °F
Melt Temperature 204 - 227 °C
399 - 441 °F
204 - 227 °C
399 - 441 °F
Mold Temperature 12.8 - 32.2 °C
55.0 - 90.0 °F
Back Pressure 0.000 - 0.552 MPa
0.000 - 80.1 psi
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Agency Ratings EU 2002/72/EC 0.5 hrs at 40C in Iso-octane
Please contact GLS Thermoplastic Elastomers for a copy of the EU compliance letter. Extraction testing was performed at an independent laboratory and conducted on injection molded plaques of said product. Test results are available from GLS Thermoplastic
EU 2002/72/EC 3 hrs at 60C in 95% ethanol
Please contact GLS Thermoplastic Elastomers for a copy of the EU compliance letter. Extraction testing was performed at an independent laboratory and conducted on injection molded plaques of said product. Test results are available from GLS Thermoplastic
FDA 21 CFR 177.2600 7hrs, 2hrs distilled water
Please contact GLS Thermoplastic Elastomers for a copy of the FDA compliance letter. Extraction testing was performed at an independent laboratory and conducted on injection molded plaques of said product. Test results are available from GLS Thermoplastic
FDA 21 CFR 177.2600 7hrs, 2hrs n-hexane
Please contact GLS Thermoplastic Elastomers for a copy of the FDA compliance letter. Extraction testing was performed at an independent laboratory and conducted on injection molded plaques of said product. Test results are available from GLS Thermoplastic
Appearance Translucent
Features Food Contact Acceptable
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Extrusion
Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%
Uses Consumer Applications
Containers
Gaskets
Kitchenware
Non-specific Food Applications
Overmolding