SABIC Innovative Plastics NORYL GTX GTX678 PPE+PA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX678 PPE+PA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be electro-statically painted or powder coated without the need for a conductive primer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.0 % | 4.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.013 - 0.015 cm/cm @Thickness 3.20 mm |
0.013 - 0.015 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.8 g/10 min @Load 5.00 kg, Temperature 300 °C |
7.8 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 300 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 12 % | 12 % | Type I, 50 mm/min; ASTM D638 |
| 12 % | 12 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 |
| 7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.90 GPa | 421 ksi | 5 mm/min; ASTM D638 |
| 2.90 GPa | 421 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.60 GPa | 377 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C |
1.31 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 78.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 83.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 191 °C | 376 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 195 °C | 383 °F | Rate B/120; ISO 306 |
| 197 °C | 387 °F | Rate B/50; ISO 306 | |
| 198 °C | 388 °F | Rate B/50; ASTM D1525 | |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4000 ohm-cm | 4000 ohm-cm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASS | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D 5302 E BLK
- S&E Specialty Polymers TufTech™ G-2184M PVC Compound
- Mid-Mountain Materials SILTEX® 1800 Amorphous Silica Industrial Textile
- Solvay GEROPON® SBL-203 Surfactant
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- ChevronTexaco Taro® 50 XL SAE 40
- ExxonMobil 100 Mobil Aviation Grease SHC
- Fainplast Compounds MPH 64 Medical Flexible PVC, Extrusion
- Arlon LW301CxxFR-P0 0.030" (0.762 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- PolyOne Geon™ Vinyl Wire & Cable W1100L-xx92FRDA Polyvinyl Chloride, Flexible (PVC, Flexible)
Copyright © lookpolymers.com All Rights Reserved