SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, strength, and flow. The material is available in limited colors for injection molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 3.8 % | 3.8 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0088 - 0.0094 cm/cm @Thickness 3.20 mm |
0.0088 - 0.0094 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0095 - 0.0101 cm/cm @Thickness 3.20 mm |
0.0095 - 0.0101 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18 g/10 min @Load 5.00 kg, Temperature 300 °C |
18 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 15 g/10 min @Load 5.00 kg, Temperature 300 °C |
15 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
| 88.0 MPa | 12800 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
| 88.0 MPa | 12800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| 7.0 % | 7.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.00 GPa | 725 ksi | 5 mm/min; ASTM D638 |
| 5.00 GPa | 725 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 145 MPa | 21000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.60 GPa | 667 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.60 GPa | 667 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.650 J/cm @Temperature -30.0 °C |
1.22 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 41.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 74.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 74.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 218 °C | 424 °F | Rate B/50; ASTM D1525 |
| 218 °C | 424 °F | Rate B/50; ISO 306 | |
| 220 °C | 428 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-1 @Thickness 0.800 mm |
V-1 @Thickness 0.0315 in |
UL 94 by SABIC-IP |
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| Glow Wire Test | 825 °C | 1520 °F | IEC 60695-2-13 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.2 kV/mm @Thickness 1.60 mm |
589 kV/in @Thickness 0.0630 in |
in air; ASTM D149 |
| 24.4 kV/mm @Thickness 1.60 mm |
620 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 |
| 400 - 600 V | 400 - 600 V | UL 746A | |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- Petroquimica Triunfo Trithene® CX 7020 LDPE - Cast Film
- SABIC Innovative Plastics Cycoloy® C4220 PC+ABS (Europe-Africa-Middle East)
- Kennametal Stellite Nistelle X Nickel Superalloy
- Shin-Etsu Silicones KF-8015 Fluid
- Solvay RHODAPEX® EST-65 Surfactant
- Wingate Alloys Tuf-Last Crosslinked PE
- ChevronTexaco HDAX® SAE 40 Low Ash Gas Engine Oil
- DuPont™ Surlyn® 8660 Ionomer Resin, Sodium
- 3M FV016405 Removable Vinyl Label Products
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 3.0 PHR MBTS
Copyright © lookpolymers.com All Rights Reserved