SABIC Innovative Plastics NORYL EN185 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL EN185 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion grade. Excellent impact strength. 185F (85C) DTUL. UL94 V-1 rated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 50 % | 50 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.27 GPa | 329 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 3.89 J/cm | 7.29 ft-lb/in | ASTM D256 |
| 1.60 J/cm @Temperature -40.0 °C |
3.00 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Gardner Impact | 13.0 J @Temperature -40.0 °C |
9.59 ft-lb @Temperature -40.0 °F |
ASTM D3029 |
| 24.0 J @Temperature -30.0 °C |
17.7 ft-lb @Temperature -22.0 °F |
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C @Temperature -40.0 - 95.0 °C |
41.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 6.40 mm |
180 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.49 mm |
V-1 @Thickness 0.0587 in |
UL 94 |
| V-0 @Thickness 2.99 mm |
V-0 @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.8 @Frequency 50.0 - 60.0 Hz |
2.8 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 24.8 kV/mm @Thickness 3.20 mm |
630 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0035 @Frequency 1.00e+6 Hz |
0.0035 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0040 @Frequency 50.0 - 60.0 Hz |
0.0040 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Radiant Panel Listing | YES | UL Tested |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO FUSE SERIES 130 CLEAR FLEXIBLE (100 Viscosity) Rapid Bonding Adhesive
- PolyOne Geon™ Vinyl Flexible D9002 Polyvinyl Chloride, Flexible (PVC, Flexible)
- MetalTek Bearium® B-10 Bearing Bronze
- Momentive Performance Materials Siloprenâ„¢ LSR 2345/03 Electrically-Conductive Liquid Silicone Rubber
- Lanxess Pocan® KU 2-7018 000000 PBT
- Haveg 41NA Phenolic; Silicate Filled
- ATI Allvac® 35N Nickel Superalloy, Heat Treatment: 1052°C (1925°F) + Age
- Amco Amalloy® B9674 Polymer Alloy
- DuPont Performance Polymers Zytel® 80G14AHS BK099 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved