BASF Ultramid® B3WGM24 HPX BK 2320 30% Glass/Mineral Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® B3WGM24 HPX BK 2320 30% Glass/Mineral Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Ultramid B3WGM24 HPX BK23210 is a very high productivity, 30% glass/mineral reinforced heat stabilized injection molding PA6 grade for components that require medium rigidity, excellent dimensional stability, low warpage out of the tool and excellent appearance.Applications: Typical applications include automobile engine covers, housings and automotive door handles.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	110 MPa	16000 psi	ISO 527
Elongation at Break	3.0 %	3.0 %	ISO 527
Tensile Modulus	7.90 GPa	1150 ksi	ISO 527
Flexural Modulus	7.96 GPa	1150 ksi	ISO 178
Izod Impact, Notched (ISO)	4.40 kJ/m² @Temperature -40.0 °C	2.09 ft-lb/in² @Temperature -40.0 °F	ISO 180
	5.20 kJ/m² @Temperature 23.0 °C	2.47 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact, Notched	0.440 J/cm²	2.09 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	210 °C	410 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	ISO 75

Processing Properties	Metric	English
Melt Temperature	270 - 295 °C	518 - 563 °F
Mold Temperature	80.0 - 95.0 °C	176 - 203 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.10 %	<= 0.10 %
Injection Pressure	35.0 - 125 MPa	5080 - 18100 psi

Descriptive Properties	Value	Comments
Color	BK 23210
Commercial Status	North America