A. Schulman POLYFORT™ PP 3726
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ PP 3726.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 29 g/10 min @Load 2.16 kg, Temperature 230 °C |
29 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | at 50 mm/min; ASTM D638 |
| Elongation at Break | 111 % | 111 % | at 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.266 GPa | 183.6 ksi | at 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.25 J/cm | 2.34 ft-lb/in | ASTM D256 |
| Gardner Impact | 31.0 J | 22.9 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N70H Nitrile Rubber
- ExxonMobil Escorene® LD-400 LDPE Medium/High Voltage Insulation (discontinued **)
- Kennametal Stellite Stellite® 6 PM cast
- Techmer ES HiFill® PA6 CM40 HS 40% Mineral Filled
- SABIC Innovative Plastics LNP THERMOCOMP DC006H PC (Asia Pacific)
- A. Schulman PP 3457-01 Copolymer Polypropylene
- Fainplast Compounds GS 69/P Flexible PVC, Injection Molding for Footwear
- Eurotec® Tecomid® NA40 KK30 NL PA 6.6 30% glass fiber/mineral reinforced, low warpage
- Formosa Plastics Formolene® LH5212 Injection Molding HDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved