- SABIC Innovative Plastics NORYL BN31 PPE+PS
SABIC Innovative Plastics NORYL BN31 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL BN31 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Blowmoldable. Excellent processability and flammability. Good heat resistance. Low temperature impact strength. Dimensional stability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| Flexural Strength | 72.0 MPa | 10400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| 1.06 J/cm @Temperature -40.0 °C |
1.99 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Gardner Impact | 13.0 J | 9.59 ft-lb | ASTM D3029 |
| 33.0 J @Temperature -40.0 °C |
24.3 ft-lb @Temperature -40.0 °F |
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 6.40 mm |
180 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 95.0 °C | 203 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 95.0 °C | 203 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV-light, water exposure/immersion | F1 | UL 746C |
Users viewing this material also viewed the following:
- Shinil Chemical SHINSTRA PA-66 W100SRB Structural Polymer Abrasion Resistance
- Samsung Cheil Industries Starex® SF-0950S MABS, Unreinforced Scratch Resistant
- CeramTec Ziralit Zirconia Toughened Alumina (ZTA), Al2O3•ZrO2
- Dow Corning SILASTIC® 24020-V NATURAL SILICONE RUBBER
- ExxonMobil PPU0009F Polypropylene Impact Copolymer
- DuPont Performance Polymers Zytel® 7304 NC010 Nylon 6 (Unverified Data**)
- Arkema Group ORGASOL® 2002 ES 3 Nat 3 Polyamide 12
- ACC QLE 1020 QSI Quantum Silicones 45 Durometer Clear, Addition Cure Elastomer for Coating
- Arkema Group Evatane® 1003 VL 4S Ethylene Vinyl Acetate
- Buckeye Polymers BP RPP 2009 GK BLK Polypropylene, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved