LyondellBasell Higlass PF062-2 Polypropylene Homopolymer, 20% Glass Fiber

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	LyondellBasell
Trade Name	Higlass
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Higlass PF062-2 Polypropylene Homopolymer, 20% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features: high melt flow, medium high modulus, chemically coupled, glass fiber-reinforced polypropylene homopolymer, high rigidity, high strength, excellent processabilityApplications: appliance parts, automotive components, electrical connectorsDescription: Higlass PF062-2 high melt flow, chemically coupled, 20% glass fiber-reinforced polypropylene homopolymer has an excellent combination of strength, stiffness and processability.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	Tool, Montell
Melt Flow	23 g/10 min @Load 2.16 kg, Temperature 230 °C	23 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	73.0 MPa	10600 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Flexural Modulus	3.40 GPa	493 ksi	Tangent at 0.05 in/min; ASTM D790A
Izod Impact, Notched	0.640 J/cm	1.20 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	156 °C	313 °F	ASTM D648