SABIC Innovative Plastics Lexan® ML3041 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® ML3041 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LEXAN ML3041 has been developed for the injection moulding of thin-wall, complex parts that require high mechanical properties and impact resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 85.0 MPa | 12300 psi | ISO 2039-1 |
| Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 105 % | 105 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 65.0 kJ/m² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.70 J/cm² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 2.00 J/cm² @Temperature -20.0 °C |
9.52 ft-lb/in² @Temperature -4.00 °F |
ISO 179/2C | |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/2C | |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 10 @Load 1.00 kg |
10 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 141 °C | 286 °F | Rate B/120; ISO 306 |
| 143 °C | 289 °F | Rate B/50; ISO 306 | |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 1.00 mm |
V-2 @Thickness 0.0394 in |
UL 94 |
| Oxygen Index | 25 % | 25 % | LOI; ISO 4589 |
| Glow Wire Test | 850 °C @Thickness 1.00 mm |
1560 °F @Thickness 0.0394 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.7 @Frequency 50.0 - 60.0 Hz |
2.7 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 27.0 kV/mm @Thickness 1.60 mm |
686 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 35.0 kV/mm @Thickness 0.800 mm |
889 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz |
0.0010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Polykemi AB POLYabs T00 ABS, Transparent
- Polykemi AB SCANMID 6 B32^ E F15 Nylon 6, Glass Fiber Reinforced, Modified
- LG Chemical SG175 ABS, Super Surface Gloss
- Ineos ABS Triax® 1220 S ABS + Polyamide Blend, Extrusion, Dry as Extruded
- Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Annealed Round
- SSAB Tunnplat Aluzink B420A Metal-coated Mild Steel
- A. Schulman POLYFORT™ PP 1930UX Extra High Flow, UV Stabilized Copolymer Polypropylene
- Eurostar Staramide AG6H PA66, 30% Glass Filled, Injection Molded
- Momentive Performance Materials PolarTherm® PT670 Boron Nitride (BN) Powder
- Abatron AboCast/AboCure 8006-11 Epoxy