| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fibre Glast Epolite 2427 Epoxy
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Fibre Glast Developments Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Viscosity | 700 cP | 700 cP | ASTM D2293 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 86 | 86 | Cured; ASTM D2240 |
| Tensile Strength at Break | 221.2 MPa | 32080 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Elongation at Break | 1.62 % | 1.62 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Tensile Modulus | 13.8 GPa | 2000 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. |
| Flexural Strength | 209.61 MPa | 30401 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Flexural Modulus | 14.7 GPa | 2130 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 60.0 °C | 140 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 120 min @Temperature 25.0 °C |
120 min @Temperature 77.0 °F |
4 fl. Oz.; ASTM D2471 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mix Ratio | 100:44 | Resin:Hardener by Weight |
| 2.13:1 | Resin:Hardener by Volume |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 HI/1 TS PA66, improved strength
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T700 12K BW Reinforced
- Omnia Plastica Akulon® PET Arnite Omnialite
- SABIC Innovative Plastics LNP THERMOCOMP PF008S PA 6
- Teknor Apex Telcar® TL-2535A Thermoplastic Elastomer
- Polyplastics Duranex® 3100H Polybutylene Terephthalate (PBT), Standard, 7.5% GF filled
- Chem Polymer Chemlon 133 G Nylon 66, 33% Glass Fiber Reinforced
- PolyOne Geon™ Vinyl Flexible XV3905 Polyvinyl Chloride, Flexible (PVC, Flexible)
- DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer (Unverified Data**)
- ExxonMobil Santoprene® 201-73W175 Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved