SABIC Innovative Plastics Lexan® HP2EU PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® HP2EU PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Melt Flow | 22 g/10 min @Load 1.20 kg, Temperature 300 °C |
22 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 21 g/10 min @Load 1.20 kg, Temperature 300 °C |
21 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
| 70.0 MPa | 10200 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| 125 % | 125 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 0.630 GPa | 91.4 ksi | 5 mm/min; ASTM D638 |
| 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| 2.35 GPa | 341 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| 0.300 J/cm @Temperature -30.0 °C |
0.562 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*3; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/2C |
| 6.50 J/cm² | 30.9 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 633 J @Temperature 23.0 °C |
467 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 139 °C | 282 °F | Rate B/50; ASTM D1525 |
| 140 °C | 284 °F | Rate B/50; ISO 306 | |
| 141 °C | 286 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 0.80 % @Thickness 2.54 mm |
<= 0.80 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 30 LS Polyamide 6, 30% Glass Fiber, UV Stabilization
- Raschig Group PiMC 1249 Sanitary, mix color
- ExxonMobil Santoprene® 241-80 Thermoplastic Elastomer (discontinued **)
- Huntsman IROGRAN® D 64 P 4777 TPU-Polyester
- Karina 700-48/1-B-IS-BZ. Black PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP QCL34 PA6.10
- SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Asia Pacific)
- Westlake EC477AA Low Density Polyethylene
- ExxonMobil Mobil Delvac Xtreme Service Grease
- DuPont Bynel® 41E712 Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved