SABIC Innovative Plastics Lexan® FXM121R PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXM121R PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC in special effects colors. Metallic and pearlescent additives. Color package may affect performance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18.2 g/10 min @Load 1.20 kg, Temperature 300 °C |
18.2 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 90 % | 90 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.2 % | 6.2 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.34 GPa | 339 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.37 GPa | 344 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 48.0 J @Temperature 23.0 °C |
35.4 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV-light, water exposure/immersion | F2 | UL 746C |
Users viewing this material also viewed the following:
- S&E Specialty Polymers G-4680E PVC
- Pyrotek TS-330 Thermoset Electrical Insulation Product
- Polymer Resources PC-GP4-[color]-1 Polycarbonate, General Purpose, Easy Flow with Mold Release
- SABIC Innovative Plastics Noryl V01505 PPE+HIPS (Asia Pacific)
- PlastxWorld CEVIAN®-N GRSJ 20% GF SAN resin
- A. Schulman POLYBATCH™ Blue Tint P40530 Concentrate Based In Homopolymer Polypropylene
- Azoty Tarnow™ TARNOFORM 300 XEC1 POM
- BASF Ultramid® A34 01 PA66 (Dry)
- Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
- ConocoPhillips 32 Ultra-Clean Super Hydraulic Oil
Copyright © lookpolymers.com All Rights Reserved