BASF Ultramid® C3UG4 20% Glass Filled PA6/66 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 20% Glass Fiber Reinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® C3UG4 20% Glass Filled PA6/66 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Halogen-free and phosphorus-free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire test up to 960°C.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.31 g/cc	0.0473 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	2.0 - 2.4 %	2.0 - 2.4 %	23°C; 50% RH; ISO 62
Viscosity Measurement	130	130	ISO 307
Melt Flow	157.2 g/10 min @Load 5.00 kg, Temperature 275 °C	157.2 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	45.0 MPa	6530 psi	50 mm/min; ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	50 mm/min; ISO 527-1/-2
Modulus of Elasticity	2.70 GPa	392 ksi	ISO 527-1/-2
Charpy Impact Unnotched	8.50 J/cm² @Temperature 23.0 °C	40.4 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU

Thermal Properties	Metric	English	Comments
Melting Point	240 °C	464 °F	DIN 53765

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	550 V	550 V	Test solution A; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	250 - 270 °C	482 - 518 °F	Injection-molding/Extrusion
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F	Injection-molding

Descriptive Properties	Value	Comments
Commercial Status	Europe