RheTech Products T15P100-00 12% Talc Reinforced Polypropylene, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products T15P100-00 12% Talc Reinforced Polypropylene, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Component housingConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 15 % | 15 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0115 cm/cm | 0.0115 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 73 | 73 | ASTM D2240 |
| Tensile Strength at Break | 32.4 MPa | 4700 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.07 GPa | 300 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C |
0.600 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.790 J | 0.583 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C | 242 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 55.2 - 103 MPa | 8000 - 15000 psi | |
| Hold Pressure | 27.6 - 51.7 MPa | 4000 - 7500 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- A. Schulman POLYBATCH™ Forest Green LL30318 Concentrate Based In LLDPE
- UBE UBEPOL BR100 Non-Oil Extended Synthetic Rubber (Raw Polymer)
- ChevronTexaco Superla® 31 White Oil
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 84A
- E-Polymers EFLEX® S3050 Overmolding
- Ascend Performance Materials Vydyne® ECO-315 Nylon 66/6, non-halogenated, ignition resistant, Conditioned
- RheTech Products GC30P104-00 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Natural
- Fainplast Compounds PM 80/A Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved