SABIC Innovative Plastics Lexan® EXL1033C PC Copolymer
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® EXL1033C PC Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan*EXL1033C polycarbonate (PC) siloxane copolymer resin is a low flow, UV stabilized grade designed for (co)-extrusion. This resin offers low temperature (-30C) ductility and excellent extrusion processing characteristics. Available in transparent and opaque colors.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.18 % @Temperature 23.0 °C |
0.18 % @Temperature 73.4 °F |
NB; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 6.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 88 | 88 | ASTM D 785 |
| Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 |
| 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 114 % | 114 % | Type I, 50 mm/min; ASTM D 638 |
| 142.4 % | 142.4 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.9 % | 5.9 % | Type I, 50 mm/min; ASTM D 638 |
| 6.2 % | 6.2 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| 2.30 GPa | 334 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.27 GPa | 329 ksi | 2 mm/min; ISO 178 |
| 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 7.20 J/cm @Temperature -30.0 °C |
13.5 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 8.93 J/cm @Temperature 23.0 °C |
16.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 23.0 kJ/m² @Temperature -30.0 °C |
10.9 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 66.0 kJ/m² @Temperature 23.0 °C |
31.4 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 2.80 J/cm² @Temperature -30.0 °C |
13.3 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 8.40 J/cm² @Temperature 23.0 °C |
40.0 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 75.0 J @Temperature 23.0 °C |
55.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 66.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 66.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 138 °C | 280 °F | Rate B/50; ISO 306 |
| 141 °C | 286 °F | Rate B/120; ISO 306 | |
| 145 °C | 293 °F | Rate B/50; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 |
| V-2 @Thickness 2.50 mm |
V-2 @Thickness 0.0984 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.7 % @Thickness 2.54 mm |
1.7 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 86 % @Thickness 2.54 mm |
86 % @Thickness 0.100 in |
ASTM D 1003 |
Users viewing this material also viewed the following:
- PTS PPE/Nylon Alloy 10% Glass Filled
- Covestro Makroblend® UT-408 Polycarbonate + Polyester Blend (discontinued **)
- Saint-Gobain CHR® M758 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
- ExxonMobil HDPE HD 6706.17 High Density Polyethylene Copolymer Resin
- Chosun Refractories CTL CGB-B Monolithic Refractories for Ladle and Tundish
- Bulk Molding Compounds BMC 1100 Corelyn Glass Fiber Reinforced Polyester Compound
- Zeon Chemicals Quintone® N180 Aliphatic Hydrocarbon Resin
- Gromax CCP PBT 6730-104F Glass/Mineral Filled
Copyright © lookpolymers.com All Rights Reserved