SABIC Innovative Plastics Lexan® BFL2015 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® BFL2015 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
on Tensile Bar; SABIC Method
0.0020 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0020 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 6.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 6.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Melt Index of Compound 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 91.0 MPa
13200 psi
Type I, 50 mm/min; ASTM D638
100 MPa
14500 psi
50 mm/min; ISO 527
Tensile Strength, Yield 92.0 MPa
13300 psi
Type I, 50 mm/min; ASTM D638
103 MPa
14900 psi
50 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
4.3 %
4.3 %
50 mm/min; ISO 527
Elongation at Yield 3.5 %
3.5 %
Type I, 50 mm/min; ASTM D638
3.6 %
3.6 %
50 mm/min; ISO 527
Tensile Modulus 4.95 GPa
718 ksi
1 mm/min; ISO 527
5.33 GPa
773 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 150 MPa
21800 psi
2 mm/min; ISO 178
156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 4.28 GPa
621 ksi
2 mm/min; ISO 178
4.60 GPa
667 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.780 J/cm
1.46 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*3; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) 80.0 kJ/m²
38.1 ft-lb/in²
80*10*3; ISO 180/1U
80.0 kJ/m²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched 6.70 J/cm²
31.9 ft-lb/in²
ISO 179/2C
10.0 J/cm²
47.6 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eU
7.50 J/cm²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
10.0 J/cm²

@Temperature -30.0 °C
 47.6 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.20 J/cm²
5.71 ft-lb/in²
ISO 179/2C
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.800 J/cm²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 61.0 J

@Temperature 23.0 °C
 45.0 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 22.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
40.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 22.2 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 22.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
40.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 22.2 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 145 °C

@Thickness 3.20 mm
 293 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
141 °C

@Thickness 3.20 mm
 286 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 148 °C
298 °F
Rate B/50; ASTM D1525
149 °C
300 °F
Rate B/50; ISO 306
150 °C
302 °F
Rate B/120; ISO 306
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
Oxygen Index 38 %
38 %
ISO 4589
Glow Wire Test 825 °C
1520 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
 3.1

@Frequency 1.00e+6 Hz
 IEC 60250
3.2

@Frequency 50.0 - 60.0 Hz
 3.2

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 20.0 kV/mm

@Thickness 1.60 mm
 508 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
Dissipation Factor 0.010

@Frequency 1.00e+6 Hz
 0.010

@Frequency 1.00e+6 Hz
 IEC 60250
0.020

@Frequency 50.0 - 60.0 Hz
 0.020

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Comparative Tracking Index 150 V
150 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES0
IEC 60695-10-2