Total HL 428 HDPE Film Grade

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer	Total Atofina
Trade Name
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Total HL 428 HDPE Film Grade.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Medium molecular weight grade. Excellent processability, excellent compatibility with LDPE and LLDPE, good tear and impact strength, good stiffness, excellent drawdown, and good moisture barrier properties.Applications: Multi-wall liners, gas flush poultry bags, mailing envelopes, heavy duty shipping sacks, fresh cut produce packaging, and coextrusions.Information provided provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Density	0.947 g/cc	0.0342 lb/in³	ASTM D792
Water Vapor Transmission	7.76 g/m²/day <br>@Thickness 0.0254 mm	0.500 g/100 in²/day <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM F1249
	10.9 g/m²/day <br>@Thickness 0.0254 mm	0.702 g/100 in²/day <br>@Thickness 0.00100 in	2.5 BUR; ASTM F1249
Thickness	25.4 microns	1.00 mil	as tested
Melt Flow	0.28 g/10 min <br>@Load 2.16 kg,<br> Temperature 190 °C	0.28 g/10 min <br>@Load 4.76 lb,<br> Temperature 374 °F	ASTM D1238
High Load Melt Index	20 g/10 min <br>@Load 21.6 kg,<br> Temperature 190 °C	20 g/10 min <br>@Load 47.6 lb,<br> Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	23.4 MPa <br>@Thickness 0.0254 mm	3400 psi <br>@Thickness 0.00100 in	2.5 BUR; ASTM D882A
	25.5 MPa <br>@Thickness 0.0254 mm	3700 psi <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D882A
Film Tensile Strength at Yield, TD	24.1 MPa <br>@Thickness 0.0254 mm	3500 psi <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D882A
	26.2 MPa <br>@Thickness 0.0254 mm	3800 psi <br>@Thickness 0.00100 in	2.5 BUR; ASTM D882A
Film Elongation at Break, MD	450 % <br>@Thickness 0.0254 mm	450 % <br>@Thickness 0.00100 in	2.5 BUR; ASTM D882A
	600 % <br>@Thickness 0.0254 mm	600 % <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D882A
Film Elongation at Break, TD	600 % <br>@Thickness 0.0254 mm	600 % <br>@Thickness 0.00100 in	2.5 BUR; ASTM D882A
	700 % <br>@Thickness 0.0254 mm	700 % <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D882A
Elmendorf Tear Strength MD	10 g <br>@Thickness 0.0254 mm	10 g <br>@Thickness 0.00100 in	2.5 BUR; ASTM D1922
	28 g <br>@Thickness 0.0254 mm	28 g <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D1922
Elmendorf Tear Strength TD	530 g <br>@Thickness 0.0254 mm	530 g <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D1922
	1450 g <br>@Thickness 0.0254 mm	1450 g <br>@Thickness 0.00100 in	2.5 BUR; ASTM D1922
Dart Drop	<= 1.97 g/micron <br>@Thickness 0.0254 mm	<= 50.0 g/mil <br>@Thickness 0.00100 in	2.5 BUR; ASTM D1709A
	3.94 g/micron <br>@Thickness 0.0254 mm	100 g/mil <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D1709A
Dart Drop Test	<= 50.0 g	<= 0.110 lb	1.0 mil; 2.5 BUR; ASTM D1709A
	100 g <br>@Thickness 0.0254 mm	0.221 lb <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D1709A
Film Tensile Strength at Break, MD	54.5 MPa <br>@Thickness 0.0254 mm	7900 psi <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D882A
	62.1 MPa <br>@Thickness 0.0254 mm	9000 psi <br>@Thickness 0.00100 in	2.5 BUR; ASTM D882A
Film Tensile Strength at Break, TD	18.6 MPa <br>@Thickness 0.0254 mm	2700 psi <br>@Thickness 0.00100 in	2.5 BUR; ASTM D882A
	39.3 MPa <br>@Thickness 0.0254 mm	5700 psi <br>@Thickness 0.00100 in	High Stalk Extrusion - 6:1 FLH/D ratio and 4:1 BUR; ASTM D882A
1% Secant Modulus, MD	710 MPa <br>@Thickness 0.0254 mm	103000 psi <br>@Thickness 0.00100 in	2.5 BUR; ASTM D882A
1% Secant Modulus, TD	1000 MPa <br>@Thickness 0.0254 mm	145000 psi <br>@Thickness 0.00100 in	2.5 BUR; ASTM D882A

Thermal Properties	Metric	English	Comments
Melting Point	131 °C	268 °F	ASTM D3417

Processing Properties	Metric	English	Comments
Melt Temperature	193 - 216 °C	380 - 420 °F	Extrusion

Descriptive Properties	Value	Comments
Process	Film
Region	US & Canada	Bamberger Polymers Distribution